3. RESULTS AND DISCUSSION3.1. Compo

3. RESULTS AND DISCUSSION
3.1. Composition of the membranes
Five membrane compositions were prepared by varying the percentages of the ion pair, while keeping the percentages of the PVC and the plasticizer equal 1:1 (table 1) The results showed that the electrode made of membrane with 10% DLX-SMA ion pair exhibits the best performance characteristics [slope 59.40 mV concentration decade-1at 25±0.1 °C , the highest value of the correlation coefficient, usable concentration range (1.0×10-5to 1.0×10-2M and detection limit 6.31×10-6
M DLX]. A typical calibration plot for electrode is shown in Fig. 2. The limit of detection, as ‎ determined from the intersection of the two extrapolated segments of the calibration ‎ graph

Hasil (Bahasa Indonesia) 2:

3. HASIL DAN PEMBAHASAN
3.1. Komposisi membran
Lima komposisi membran disiapkan dengan memvariasikan persentase dari pasangan ion, sambil menjaga persentase dari PVC dan plasticizer sama 1: 1 (tabel 1) Hasil penelitian menunjukkan bahwa elektroda yang terbuat dari membran dengan 10% DLX- pasangan ion SMA menunjukkan karakteristik kinerja terbaik [kemiringan 59,40 mV konsentrasi dekade-1at 25 ± 0,1 ° C, nilai tertinggi dari koefisien korelasi, rentang konsentrasi yang dapat digunakan (1,0 × 1,0 × 10-2M 10-5to dan deteksi batas 6.31 × 10 -6
M DLX]. Sebuah kalibrasi petak khas untuk elektroda ditunjukkan pada Gambar. 2. Batas deteksi, seperti yang ditetapkan dari persimpangan dua segmen diekstrapolasi dari grafik kalibrasi