Effect of inoculation and casting m

Effect of inoculation and casting modulus on the
microstructure and mechanical properties of ductile
NI-resist cast iron

Ductile Ni-resist cast iron (type D-5S) which is normally used in exhaust manifold in automotive
industries mainly contains up to 29 wt% nickel, 4.9 wt% silicon and 1.7 wt% chromium. In this
study, the microstructure and mechanical properties of as cast ductile Ni-resist cast iron have
been investigated at room temperature. The microstructure consists of graphite nodules
embedded in austenitic matrix and carbides. The FeNi3 phase also found in the austenitic matrix.
By adding inoculant, carbide formation tendency decreased and led to subsequent decrease of the
hardness. Furthermore, tensile properties improved by inoculation exhibiting ultimate tensile
strength and yield strength from the range of 273-303 MPa and 207-255 MPa for samples
without inoculant to respectively 285-449 MPa and 260-334 MPa for inoculated samples.

Hasil (Bahasa Indonesia) 2:

Pengaruh inokulasi dan casting modulus pada
struktur mikro dan sifat mekanik dari ulet
NI-menolak besi cor ulet Ni-resist besi cor (tipe D-5S) yang biasanya digunakan dalam exhaust manifold di otomotif industri terutama berisi hingga 29% berat nikel, 4,9% berat silikon dan 1,7% berat kromium. Dalam studi, struktur mikro dan sifat mekanik sebagai ulet cor Ni-resist besi cor telah diteliti pada suhu kamar. Mikro terdiri dari nodul grafit tertanam dalam matriks austenitik dan karbida. The FeNi3 fase juga ditemukan dalam matriks austenitik. Dengan menambahkan inokulan, pembentukan karbida kecenderungan menurun dan menyebabkan penurunan berikutnya dari kekerasan. Selanjutnya, sifat tarik ditingkatkan dengan inokulasi menunjukkan tarik utama kekuatan dan menghasilkan kekuatan dari berbagai 273-303 MPa dan 207-255 MPa untuk sampel tanpa inokulan untuk masing-masing 285-449 MPa dan 260-334 MPa untuk sampel diinokulasi.