Nanocomposites composed of unsatura

Nanocomposites composed of unsaturated polyester matrix and organically modified clay
filler were prepared. After the synthesis, XRD patterns showed that the interlayer spacing
expanded from 1.25 nm to 4.5 nm. The mechanical properties of the nanocomposites were
determined and it was found that adding only 3 w/w % organically modified clay improved the
flexural modulus of unsaturated polyester by 35%. From DSC diagrams, it was found that Tg
values of the nanocomposites also increased with the clay content. It is concluded that partially
exfoliated / intercalated nanocomposites were formed at relatively low clay contents.

Hasil (Bahasa Indonesia) 2:

Nanocomposites terdiri dari tak jenuh matriks poliester dan dimodifikasi secara organik tanah liat
filler disiapkan. Setelah sintesis, pola XRD menunjukkan bahwa jarak interlayer
diperluas dari 1,25 nm menjadi 4,5 nm. Sifat mekanis dari nanocomposites yang
ditentukan dan ditemukan bahwa menambahkan hanya 3 w / w% tanah liat organik diubah meningkatkan
modulus lentur poliester tak jenuh sebesar 35%. Dari diagram DSC, ditemukan bahwa Tg
nilai dari nanocomposites juga meningkat dengan kandungan clay. Disimpulkan bahwa sebagian
dikelupas / nanocomposites diselingi terbentuk pada isi tanah liat yang relatif rendah.