The effect of commercial additive S

The effect of commercial additive Sasobit wax (S) on the viscosity characteristics of bitumen 60/70-penetration grade is
yet to be fully understood. The viscosity of bitumen is the measure of its resistance to flow which affects workability, and
resistance to deformation of the mixture. This study reviewed the bitumen modification process in relation to warm mix
asphalt (WMA) technology, using S as a modifier. The study investigated the viscosity measurements of modified
bitumen, using the Brookfield viscometer. The binders mixed with various percentage of the wax S 1%, 2%, 3%, 4%and
5% were investigated. The results from the study showed the viscosity of the binder decreasing at higher temperatures
while at midrange temperatures the viscosity increases with an increase in the additive. This study has provided a valuable
data on the effect of the additive S on increasing the dynamic viscosity of the binder at low temperature and decreasing the
kinematic viscosity at high temperature, been attributed to the presence of the S wax with high hydrocarbons molecular
content in the binder, which is expected to improve the viscosity properties of the modified binder and enhance its
resistance to deformation when used in warm asphalt concrete mixtures.

Hasil (Bahasa Indonesia) 1:

Efek komersial aditif Sasobit lilin (S) di viskositas karakteristik aspal 60/70-penetrasi kelasNamun untuk sepenuhnya dipahami. Viskositas aspal adalah ukuran ketahanan terhadap aliran yang mempengaruhi dilaksanakan, dantahan terhadap deformasi campuran. Studi ini ditinjau proses modifikasi aspal sehubungan dengan campuran hangataspal teknologi (WMA), menggunakan S sebagai pengubah. Studi diselidiki pengukuran viskositas dimodifikasiaspal, menggunakan Brookfield viscometer. Binder dicampur dengan berbagai persentase lilin S 1%, 2%, 3%, 4% dan5% diselidiki. Hasil dari studi menunjukkan viskositas pengikat menurun pada suhu tinggisementara pada midrange suhu viskositas meningkat dengan peningkatan aditif. Studi ini telah memberikan yang berhargadata pada efek S aditif di meningkatkan viskositas dinamis pengikat pada suhu rendah dan penurunanViskositas kinematis pada suhu tinggi, telah dikaitkan dengan kehadiran lilin S dengan tinggi hidrokarbon molekulerkonten dalam binder, yang diharapkan dapat meningkatkan sifat kekentalan pengikat dimodifikasi dan meningkatkan nyatahan terhadap deformasi bila digunakan dalam campuran beton aspal hangat.