In this study, the sliding wear res

In this study, the sliding wear resistance behaviour of hot-dip galvanized and zinc-iron electrodeposited coatings, against an alumina pin in a pin-on-disc set-up immersed in a NaCl solution is investigated. During wear tests, the evolution of the open-circuit corrosion potential was monitored. The behaviour of both coatings is compared in terms of open-circuit corrosion potential, friction coefficient and loss of mass after sliding

Hasil (Bahasa Indonesia) 1:

Dalam studi ini, geser memakai perilaku perlawanan hot-dip galvanis dan seng-besi Elektrodeposisi coating, terhadap alumina pin di set-up pin pada disk yang direndam dalam larutan NaCl diselidiki. Selama tes memakai, evolusi korosi sirkuit terbuka potensi dipantau. Perilaku lapisan kedua dibandingkan sirkuit terbuka korosi potensial, Koefisien gesekan dan hilangnya massa setelah geser

Hasil (Bahasa Indonesia) 2:

Dalam penelitian ini, geser perilaku ketahanan aus dari hot-dip galvanis dan seng-besi Elektrodeposisi pelapis, melawan pin alumina di pin-on-disc set-up direndam dalam larutan NaCl diselidiki. Selama tes pakai, evolusi potensi korosi sirkuit terbuka dipantau. Perilaku kedua pelapis dibandingkan dalam hal potensi korosi sirkuit terbuka, koefisien gesekan dan hilangnya massa setelah meluncur