A constant vertical load was applie

A constant vertical load was applied to the samples with a testing machine, which was
insulated using kaowool. Fume extraction was provided. All samples tested were 10 mm
thick by 100 mm wide. This enabled a region 100 mm square to be exposed to the heat flux.
For the tensile loading, 40 mm long samples were loaded using the wedge grips of the
testing machine. In this mode it was necessary to insulate the upper grip with about 15 mm
thick kaowool to prevent it from overheating, and resulting in premature grip slippage

Hasil (Bahasa Indonesia) 1:

Beban vertikal konstan diaplikasikan pada sampel dengan mesin pengujian, yangterisolasi dengan menggunakan kaowool. Asap ekstraksi disediakan. Semua sampel yang diuji adalah 10 mmtebal dengan lebar 100 mm. Ini memungkinkan 100 mm persegi wilayah akan terkena fluks panas.Untuk pemuatan tarik, 40 mm panjang sampel sarat menggunakan genggaman bajiMesin pengujian. Dalam mode ini itu diperlukan untuk mengisolasi pegangan atas dengan 15 mmkaowool tebal untuk mencegah overheating, dan mengakibatkan prematur pegangan selip

Hasil (Bahasa Indonesia) 2:

Sebuah beban vertikal konstan diaplikasikan pada sampel dengan mesin uji, yang
terisolasi menggunakan kaowool. Ekstraksi asap diberikan. Semua sampel yang diuji adalah 10 mm
tebal dengan lebar 100 mm. Ini memungkinkan wilayah 100 mm persegi untuk terkena fluks panas.
Untuk pemuatan tarik, 40 mm sampel panjang yang dimuat menggunakan grip wedge dari
mesin uji. Dalam mode ini itu perlu untuk melindungi pegangan atas dengan sekitar 15 mm
kaowool tebal untuk mencegah dari overheating, dan mengakibatkan dini pegangan slip