Surprisingly, the melting temperatu

Surprisingly, the melting temperature of plasticized PLA/
Na-MMT did not improve. Then, the melting temperature
decreased slightly from 167.72 °C to 167.26 °C. On the
other hand, the crystallinity degree of plasticized PLA
increased from 17.7% to 34.6%. Thermal properties of
plasticized PLA/Na-MMT are shown in Figure 3. It can
be seen that the presence of Na-MMT improved the
thermal properties

Hasil (Bahasa Indonesia) 1:

Anehnya, suhu mencair plasticized PLA /Na-MMT tidak membaik. Kemudian, suhu mencairmenurun sedikit dari 167.72 ° C hingga 167.26 ° C. Padasisi lain, tingkat bagian plasticized PLAmeningkat dari 17.7% 34.6%. Sifat termalplasticized PLA/Na-MMT ditunjukkan dalam gambar 3. Itu bisadilihat bahwa kehadiran Na-MMT meningkatCiri-ciri termal

Hasil (Bahasa Indonesia) 2:

Anehnya, suhu leleh plasticized PLA /
Na-MMT tidak membaik. Kemudian, suhu leleh
sedikit menurun dari 167,72 ° C untuk 167,26 ° C. Di
sisi lain, tingkat kristalinitas plasticized PLA
meningkat dari 17,7% menjadi 34,6%. Sifat termal
plasticized PLA / Na-MMT ditunjukkan pada Gambar 3. Hal ini dapat
dilihat bahwa kehadiran Na-MMT meningkatkan
sifat termal