Polymer/organically modi®ed layered silicate (PLS) nanocomposites are a new class of ®lled polymers with ultra®ne phase
dimensions. They offer an outstanding combination of stiffness, strength and weight that is dif®cult to attain separately from
the individual components. Additionally, the nanoscopic phase distribution as well as synergism between polymer and the
layered silicate result in additional properties, such as ¯ame retardency, enhanced barrier properties and ablation resistance,
which are not observed in either component. These nanocomposites are synthesized by blending the organically modi®ed
layered silicate (OLS) into the polymer melt. Thus, understanding the relationship between the molecular structure and the
thermal stability (decomposition temperature, rate, and the degradation products) of the organic modi®cation of the layered
silicate is critical. During this study, modern thermal analysis techniques combined with infrared spectroscopy and mass
spectrometry (TGA±FTIR±MS) were used to obtain information on the thermal stability and degradation products. The effect
of chemical variation (alkyl chain length, number of alkyls, and unsaturation) of organic modi®ers on the thermal stability of
the organically exchanged montmorillonite are discussed. A range of interesting results is observed, however, not all are
currently understandable. # 2001 Elsevier Science B.V. All rights reserved
0/5000
Dari: -
Ke: -
Hasil (Bahasa Indonesia) 1: [Salinan]
Disalin!
Polimer/organik modi® ed berlapis silikat (PLS) nanocomposites adalah kelas baru® lled polimer dengan ultra® ne fasedimensi. Mereka menawarkan sebuah kombinasi yang luar biasa dari kekakuan, kekuatan dan berat yang béda® kultus untuk mencapai secara terpisah darimasing-masing komponen. Selain itu, nanoscopic tahap distribusi serta sinergi antara polimer danberlapis silikat mengakibatkan sifat tambahan, seperti ¯ame retardency, meningkatkan penghalang properti dan ablasi perlawanan,yang tidak diamati dalam komponen baik. Nanocomposites ini disintesis oleh pencampuran organik modi® edberlapis silikat (OLS) ke dalam polimer meleleh. Dengan demikian, memahami hubungan antara struktur molekul danstabilitas termal (suhu dekomposisi, tingkat, dan hasil degradasi) modi organik® kation dari berlapissilikat penting. Selama studi ini, teknik modern termal analisis dikombinasikan dengan Spektroskopi Inframerah dan massaspektrometri (TGA±FTIR±MS) digunakan untuk mendapatkan informasi mengenai produk stabilitas dan degradasi termal. Efekdari variasi kimia (panjang rantai alkil, jumlah alkyls, dan unsaturation) organik modi® ers pada stabilitas termalmineral-montmorilonite organik bertukar dibahas. Berbagai hasil yang menarik diamati, namun, tidak semua yangsaat ini dapat dimengerti. # 2001 Elsevier ilmu BV Semua Hak, Milik
Sedang diterjemahkan, harap tunggu..
Hasil (Bahasa Indonesia) 2:[Salinan]
Disalin!
/ Organik modi®ed silikat berlapis (PLS) nanocomposites polimer kelas baru polimer ®lled dengan fase ultra®ne
dimensi. Mereka menawarkan kombinasi yang luar biasa dari kekakuan, kekuatan dan berat badan yang dif®cult untuk mencapai secara terpisah dari
masing-masing komponen. Selain itu, distribusi fase nanoscopic serta sinergisme antara polimer dan
hasil silikat berlapis sifat tambahan, seperti Ame retardency, sifat penghalang ditingkatkan dan resistance ablasi,
yang tidak diamati dalam komponen baik. Nanocomposites ini disintesis dengan memadukan organik modi®ed
silikat berlapis (OLS) ke dalam lelehan polimer. Dengan demikian, memahami hubungan antara struktur molekul dan
stabilitas termal (suhu dekomposisi, tingkat, dan produk degradasi) dari modi®cation organik dari berlapis
silikat sangat penting. Selama penelitian ini, teknik analisis termal modern yang dikombinasikan dengan spektroskopi inframerah dan massa
spektrometri (TGA ± FTIR ± MS) yang digunakan untuk memperoleh informasi tentang thermal stabilitas dan degradasi produk. Pengaruh
variasi kimia (alkil panjang rantai, jumlah alkil, dan jenuh) dari modi®ers organik pada stabilitas termal
yang organik dipertukarkan montmorillonite dibahas. Berbagai hasil yang menarik diamati, bagaimanapun, tidak semua yang
saat ini dipahami. # 2001 Elsevier Science BV All rights reserved
Sedang diterjemahkan, harap tunggu..
 
Bahasa lainnya
Dukungan alat penerjemahan: Afrikans, Albania, Amhara, Arab, Armenia, Azerbaijan, Bahasa Indonesia, Basque, Belanda, Belarussia, Bengali, Bosnia, Bulgaria, Burma, Cebuano, Ceko, Chichewa, China, Cina Tradisional, Denmark, Deteksi bahasa, Esperanto, Estonia, Farsi, Finlandia, Frisia, Gaelig, Gaelik Skotlandia, Galisia, Georgia, Gujarati, Hausa, Hawaii, Hindi, Hmong, Ibrani, Igbo, Inggris, Islan, Italia, Jawa, Jepang, Jerman, Kannada, Katala, Kazak, Khmer, Kinyarwanda, Kirghiz, Klingon, Korea, Korsika, Kreol Haiti, Kroat, Kurdi, Laos, Latin, Latvia, Lituania, Luksemburg, Magyar, Makedonia, Malagasi, Malayalam, Malta, Maori, Marathi, Melayu, Mongol, Nepal, Norsk, Odia (Oriya), Pashto, Polandia, Portugis, Prancis, Punjabi, Rumania, Rusia, Samoa, Serb, Sesotho, Shona, Sindhi, Sinhala, Slovakia, Slovenia, Somali, Spanyol, Sunda, Swahili, Swensk, Tagalog, Tajik, Tamil, Tatar, Telugu, Thai, Turki, Turkmen, Ukraina, Urdu, Uyghur, Uzbek, Vietnam, Wales, Xhosa, Yiddi, Yoruba, Yunani, Zulu, Bahasa terjemahan.

Copyright ©2025 I Love Translation. All reserved.

E-mail: