Thermal decomposition of unsaturate

Thermal decomposition of unsaturated polyester and TCNP composite has been investigated by thermogravemetry
method UPE And UPE/TCNP degraded in two stages and 95– 97% of original mass is decomposed into volatiles rather
than char volatiles with . The kinetics parameter, activation energy, and reaction rate constant as well as
thermodynamics property was found to be higher than composites, however the reason is the presence on iron nano size
in TCNP powder which enhances the pyrolysis reaction.

Hasil (Bahasa Indonesia) 1:

Dekomposisi termal polyester tak jenuh dan komposit TCNP telah diselidiki oleh thermogravemetry metode PDU dan PDU/TCNP rusak dalam dua tahap dan 95-97% massa asli didekomposisi ke volatil agak daripada char volatil dengan. Kinetika parameter, aktivasi energi, dan reaksi menilai konstan serta termodinamika properti ditemukan untuk menjadi lebih tinggi daripada komposit, namun alasan adanya berukuran nano besi dalam TCNP bubuk yang meningkatkan reaksi pirolisis.

Hasil (Bahasa Indonesia) 2:

Dekomposisi termal dari poliester tak jenuh dan TCNP komposit telah diteliti oleh thermogravemetry
metode PDU Dan PDU / TCNP terdegradasi dalam dua tahap dan 95- 97% dari massa asli didekomposisi menjadi volatil bukan
dari volatil char dengan. Kinetika parameter, energi aktivasi, dan konstanta laju reaksi serta
properti termodinamika ditemukan lebih tinggi dari komposit, namun alasannya adalah kehadiran pada ukuran nano besi
dalam bubuk TCNP yang meningkatkan reaksi pirolisis.