Both magnetic heads and disks are t

Both magnetic heads and disks are those for
40 GB/platter disk drives. The magnetic heads were
made of pico-sized AlTiC slider with 40-A˚ thick carbon
overcoat (COC). The slider had a sub-ambient
pressure airbearing with a nominal mean FH of 12–
13 nm. The magnetic disks were made from aluminum
alloy substrate with Co–Cr–Pt alloy magnetic layer.
The disks were coated with _25-A˚ thick COC and
_12-A˚ thick PFPE Z-dol lubricant. The COC on magnetic
disk had a resistivity of _106 Wcm, measured
with CV map system using a mercury probe.

Hasil (Bahasa Indonesia) 1:

Magnetic kepala dan disk adalah orang-orang untuk40 GB piring disk drive. Kepala-kepala magnetikterbuat dari berukuran pico AlTiC slider dengan berkarbon tebal 40-A˚mantel (COC). Slider telah sub ambientekanan airbearing dengan FH berarti nominal 12-13 nm. Disk magnetik yang terbuat dari aluminiumpaduan substrat dengan lapisan magnetic paduan Co-Cr-Pt.Disk dilapisi dengan _25-A˚ tebal COC dan_12-A˚ PFPE Z-dol tebal pelumas. COC pada magnetikdisk telah resistivitas _106 Wcm, diukurdengan sistem peta CV menggunakan mercury probe.

Hasil (Bahasa Indonesia) 2:

Kedua kepala magnetik dan disk adalah mereka untuk
40 GB / platter disk drive. Kepala magnetik yang
terbuat dari pico berukuran slider AlTiC dengan 40-karbon tebal
mantel (COC). Slider memiliki sub-ambient
tekanan airbearing dengan rata FH nominal 12-
13 nm. Disk magnetik yang terbuat dari aluminium
alloy substrat dengan Co-Cr-Pt paduan lapisan magnetik.
Disk dilapisi dengan COC tebal _25-A dan
_12-tebal PFPE Z-dol pelumas. COC pada magnetic
disk yang memiliki resistivitas _106 Wcm, diukur
dengan sistem peta CV menggunakan probe merkuri.