Multiwalled carbon nanotubes (MWCNTs) were used as doping material for three-dimensional chitosan scaffolds
to develop a highly conductive, porous, and biocompatible composite material. The porous and interconnected structures
were formed by the process of thermally induced phase separation followed by freeze-drying applied to an aqueous
solution of 1 wt % chitosan acetic acid. The porosity was characterized to be 97% by both mercury intrusion porosimetry
measurements and SEM image analysis. When MWCNTs were used as a filler to introduce conductive pathways
throughout the chitosan skeleton, the solubilizing hydrophobic and hydrophilic properties of chitosan established
stable polymer/MWCNT solutions that yielded a homogeneous distribution of nanotubes throughout the final composite
matrix. A percolation theory threshold of∼2.5 wt % MWCNTs was determined by measurement of the conductivity
as a function of chitosan/MWCNT ratios. The powder resistivity of completely compressed scaffolds also was measured
and was found to be similar for all MWCNT concentrations (0.7-0.15Ωcm powder resistivity for MWCNTs of 0.8-5
wt %) and almost five times lower than the 20 kΩcm value found for pure chitosan scaffolds.

Hasil (Bahasa Indonesia) 1:

Nanotubes karbon Multiwalled (MWCNTs) digunakan sebagai doping bahan untuk tiga dimensi chitosan perancahuntuk mengembangkan material komposit yang sangat konduktif, berpori dan biokompatibel. Struktur berpori dan saling berhubungandibentuk oleh proses pemisahan thermally induksi fase yang diikuti oleh freeze-drying diterapkan berairlarutan asam asetat 1 wt % chitosan. Porositas ditandai 97% dengan kedua Merkurius intrusi porosimetrypengukuran dan analisis gambar SEM. Ketika MWCNTs digunakan sebagai pengisi untuk memperkenalkan konduktif jalurseluruh kerangka chitosan, solubilizing hidrofobik dan hidrofil sifat chitosan didirikansolusi polimer/MWCNT stabil yang menghasilkan distribusi homogen dari nanotubes seluruh komposit akhirmatriks. Perkolasi teori ambang of∼2.5 wt % MWCNTs ditentukan oleh pengukuran konduktivitassebagai fungsi dari chitosan MWCNT rasio. Resistivitas bubuk sepenuhnya terkompresi perancah juga diukurdan ditemukan untuk menjadi serupa untuk semua konsentrasi MWCNT (0.7-0.15Ωcm bubuk resistivitas untuk MWCNTs 0,8-5WT %) dan hampir lima kali lebih rendah dari nilai 20 kΩcm yang ditemukan untuk perancah murni chitosan.