4. ConclusionThe high-yield synthes

4. Conclusion

The high-yield synthesis of stoichiometric BN nanostructures using borazine gas as chemical precursor and the HFCVD technique has been demonstrated. The structure, morphology, and chemical composition of these nanostructures were studied. The BN nanostructures include quasispherical nanoparticles with sizes ranging between 20 and 50 nanometers and nanofibers of the same diameter that measure from 80 to 500 nanometers in length. There is no evidence of elemental B phase segregation or N deficiency. The comprehensive characterization study done indicates that all of the powder material obtained is stoichiometric BN mainly in the hexagonal and rhombohedral phases. Therefore, this study has resulted in the development of a new method to achieve the high-yield synthesis of stoichiometric BN nanostructures that can be employed to enhance the strength of structural materials of industrial applications.

Acknowledgments

The authors wish to acknowledge the financial support of NASA URC (NNX08BA48A) and PR NASA EPSCoR RID (NNX07AO30A). They also thank Josue Ortiz (SEM), Oscar Resto and Javier Avalos (MET), Neiza Hernandez (FTIR), and Esteban Fachini (XPS). Piazza thanks the Secretary of State of Higher Education, Science and Technology (SEESCYT) of the Dominican Republic (2007 and 2008 FONDOCYT program) and the Pontificia Universidad Catolica Madre y Maestra (2007-2008 Grants for Research).

doi: 10.1155/2009/429360

Hasil (Bahasa Indonesia) 1:

4. kesimpulanSintesis nanostructures BN stoikiometri menggunakan borazine gas sebagai pendahulu kimia dan teknik HFCVD imbal hasil yang tinggi telah dibuktikan. Struktur, morfologi, dan komposisi kimia nanostructures ini dipelajari. BN nanostructures termasuk partikel nano quasispherical dengan ukuran berkisar antara 20 dan 50 nanometer dan nanofibers diameter yang sama yang mengukur dari 80 untuk 500 nanometer panjang. Tidak terdapat bukti elemen B fasa pemisahan atau N kekurangan. Studi komprehensif karakterisasi dilakukan menunjukkan bahwa semua material serbuk yang diperoleh adalah stoikiometri BN terutama dalam fase heksagonal dan rhombohedral. Oleh karena itu, penelitian ini telah mengakibatkan pengembangan metode baru untuk mencapai imbal hasil yang tinggi sintesis stoikiometri BN nanostructures yang dapat digunakan untuk meningkatkan kekuatan bahan struktural aplikasi industri.Ucapan terima kasihPenulis ingin mengakui dukungan keuangan dari NASA URC (NNX08BA48A) dan PR NASA EPSCoR sembuh (NNX07AO30A). Mereka juga terima Josue Ortiz (SEM), Oscar Resto dan Javier Avalos (MET), Neiza Hernandez (FTIR), dan Esteban Fachini (XPS). Piazza terima kasih Sekretaris Negara pendidikan tinggi, ilmu pengetahuan dan teknologi (SEESCYT) dari Republik Dominika (2007 dan 2008 FONDOCYT program) dan Pontificia Universidad Catolica Madre y Maestra (2007-2008 hibah untuk penelitian).Doi: 10.1155/2009/429360

Hasil (Bahasa Indonesia) 2:

4. Kesimpulan

Sintesis-hasil tinggi struktur nano BN stoikiometri menggunakan gas borazine sebagai prekursor kimia dan teknik HFCVD telah dibuktikan. Struktur, Komposisi morfologi, dan kimia dari struktur nano dipelajari. BN struktur nano termasuk nanopartikel quasispherical dengan ukuran berkisar antara 20 dan 50 nanometer dan nanofibers dengan diameter yang sama yang mengukur 80-500 nanometer panjang. Tidak ada bukti dari pemisahan fase B elemental atau kekurangan N. Studi karakterisasi komprehensif dilakukan menunjukkan bahwa semua bahan serbuk yang diperoleh adalah stoikiometri BN terutama di fase heksagonal dan rhombohedral. Oleh karena itu, penelitian ini telah menghasilkan pengembangan metode baru untuk mencapai sintesis-yield tinggi struktur nano BN stoikiometri yang dapat digunakan untuk meningkatkan kekuatan bahan struktural aplikasi industri.

Ucapan Terima Kasih

Para penulis ingin mengakui dukungan keuangan dari NASA URC (NNX08BA48A) dan PR NASA EPSCoR RID (NNX07AO30A). Mereka juga terima Josue Ortiz (SEM), Oscar Resto dan Javier Avalos (MET), Neiza Hernandez (FTIR), dan Esteban fachini (XPS). Piazza berkat Sekretaris Negara Pendidikan Tinggi, Sains dan Teknologi (SEESCYT) Republik Dominika (2007 dan 2008 Program FONDOCYT) dan Pontificia Universidad Catolica Madre y Maestra (2007-2008 Hibah Penelitian).

Doi: 10,1155 / 2009 / 429.360