Introducing unmodified organically

Introducing unmodified organically clay/Na-montmorillonite (Na-MMT) was applied into plasticized poly(lactic acid)
PLA to produce film composites by direct casting. Film composite structure, the crystallinity degree and form, and
thermal properties were carried out using X-ray diffraction and differential scanning calorimetry. The effect of Na-
MMT to the tortuous path and the crystallinity degree in the plasticized film composites were calculated in oxygen
barrier properties. Chromatogram film composites resulted in an intercalated structure that showed peak diffraction
angle shift at about 0.2o. Then, a peak diffraction pattern was indicated in α-form crystal structure. Plasticized PLA has
a crystallinity degree at 34%, and the addition of Na-MMT increased to 52%. Glass transition temperature improved
from 53 °C to 57 °C, and melting temperature remained stable at 167 °C. Filling Na-MMT into plasticized PLA caused
to enhance a tortuous path about 28% and improved the oxygen permeability to 80%. As a result, the addition of Na-
MMT of 3% into plasticized PLA during film composite preparation using the mixing method resulted in balancing
properties related to the crystallinity degree, thermal properties, and oxygen barrier properties.

Hasil (Bahasa Indonesia) 1:

Memperkenalkan unmodified organik tanah liat/Na-mineral montmorilonite (Na-MMT) diterapkan ke plasticized Poli (laktat asam)PLA untuk memproduksi film komposit oleh pengecoran langsung. Film struktur gabungan, bentuk, dan tingkat bagian danCiri-ciri termal dilakukan menggunakan Difraksi sinar x dan Diferensial pemindaian kalorimetri. Efek Na-MMT jalan berliku-liku dan gelar bagian dalam plasticized film komposit dihitung dalam oksigensifat penghalang. Chromatogram film komposit mengakibatkan struktur intercalated yang menunjukkan puncak Difraksisudut shift di sekitar 0.2o. Kemudian, pola Difraksi puncak telah ditunjukkan dalam struktur kristal α-bentuk. Plasticized PLA telahgelar bagian di 34%, dan penambahan Na-MMT meningkat menjadi 52%. Temperatur transisi gelas ditingkatkandari 53 ° C sampai 57 ° C, dan temperatur leleh tetap stabil pada 167 ° C. Mengisi Na-MMT ke dalam plasticized PLA disebabkanuntuk meningkatkan jalan berliku-liku sekitar 28% dan meningkatkan permeabilitas oksigen untuk 80%. Sebagai hasilnya, penambahan Na-MMT 3% menjadi plasticized PLA selama persiapan komposit film menggunakan metode pencampuran mengakibatkan menyeimbangkanProperti terkait dengan bagian derajat, sifat termal, dan oksigen penghalang properti.

Hasil (Bahasa Indonesia) 2:

Memperkenalkan dimodifikasi secara organik tanah liat / Na-montmorillonit (Na-MMT) diaplikasikan ke poli plasticized (asam laktat)
PLA untuk menghasilkan komposit film oleh pengecoran langsung. Film struktur komposit, tingkat kristalinitas dan bentuk, dan
sifat termal dilakukan dengan menggunakan difraksi sinar-X dan pemindaian termogram. Pengaruh Na-
MMT ke jalan berliku-liku dan tingkat kristalinitas dalam komposit Film plasticized dihitung oksigen
sifat penghalang. Kromatogram komposit Film mengakibatkan struktur diselingi yang menunjukkan puncak difraksi
pergeseran sudut di sekitar 0.2o. Kemudian, pola puncak difraksi ditunjukkan dalam struktur kristal α-bentuk. Plasticized PLA memiliki
gelar kristalinitas pada 34%, dan penambahan Na-MMT meningkat menjadi 52%.
Kaca suhu transisi meningkat dari 53 ° C menjadi 57 ° C, dan suhu leleh tetap stabil pada 167 ° C. Mengisi Na-MMT ke plasticized PLA disebabkan
untuk meningkatkan jalan berliku-liku sekitar 28% dan meningkatkan permeabilitas oksigen ke 80%. Akibatnya, penambahan Na-
MMT dari 3% menjadi plasticized PLA selama persiapan komposit Film menggunakan metode pencampuran mengakibatkan menyeimbangkan
sifat berkaitan dengan tingkat kristalinitas, sifat termal, dan sifat penghalang oksigen.