Thermal properties of plasticizedPL

Thermal properties of plasticized
PLA/NA-MMT were measured including glass transition
temperature (Tg), melting temperature (Tm), enthalphy
fusion (ΔHm) and the crystallinity degree (X). Previous
research showed that plasticized PLA using PEG400
decreased glass enthalphy fusion (ΔHm) and the
crystallinity degree (X). Previous research showed that
plasticized PLA using PEG400 decreased glass transition
temperature and melting temperature. Neat PLA was
recorded having a Tg about 58.5 °C and plasticized PLA
fell to 53.2 °C. Then, melting temperature decreased
slightly from 167.72 °C to 167.26 °C. On the other
hand, the crystallinity degree of plasticized PLA increased
from 17.7% to 34.6% [6

0/5000

Dari: -

Ke: -

Hasil (Bahasa Indonesia) 1: [Salinan]

Disalin!

Termal sifat eksklusif plasticizedPLA/NA-MMT diukur termasuk kaca transisisuhu (Tg), mencair suhu (Tm), enthalphyFusion (ΔHm) dan tingkat bagian (X). Sebelumnyapenelitian menunjukkan bahwa eksklusif plasticized PLA menggunakan PEG400menurun kaca enthalphy fusion (ΔHm) danBagian derajat (X). Penelitian sebelumnya menunjukkan bahwaPLA plasticized menggunakan PEG400 menurun kaca transisisuhu dan suhu mencair. Rapi PLA adalahtercatat memiliki Tg sekitar 58,5 ° C dan eksklusif plasticized PLAjatuh ke 53.2 ° C. Kemudian, temperatur leleh menurunsedikit dari 167.72 ° C hingga 167.26 ° C. Di sisi laintangan, tingkat bagian plasticized PLA meningkatdari 17.7% 34.6% [6

Sedang diterjemahkan, harap tunggu..

Hasil (Bahasa Indonesia) 2:[Salinan]

Disalin!

Sifat termal plasticized
PLA / NA-MMT diukur termasuk kaca transisi
suhu (Tg), suhu leleh (Tm), enthalpy
fusion (ΔHm) dan derajat kristalinitas (X). Sebelumnya
penelitian menunjukkan bahwa plasticized PLA menggunakan PEG400
menurun kaca enthalpy fusion (ΔHm) dan
derajat kristalinitas (X). Penelitian sebelumnya menunjukkan bahwa
plasticized PLA menggunakan PEG400 menurun transisi gelas
suhu dan temperatur leleh. Rapi PLA telah
tercatat memiliki Tg sekitar 58,5 ° C dan plasticized PLA
jatuh ke 53,2 ° C. Kemudian, suhu mencair menurun
sedikit dari 167,72 ° C untuk 167,26 ° C. Di lain
pihak, tingkat kristalinitas plasticized PLA meningkat
dari 17,7% menjadi 34,6% [6

Sedang diterjemahkan, harap tunggu..

Hasil (Bahasa Indonesia) 3:[Salinan]

Disalin!

Sedang diterjemahkan, harap tunggu..

Bahasa lainnya

Dukungan alat penerjemahan: Afrikans, Albania, Amhara, Arab, Armenia, Azerbaijan, Bahasa Indonesia, Basque, Belanda, Belarussia, Bengali, Bosnia, Bulgaria, Burma, Cebuano, Ceko, Chichewa, China, Cina Tradisional, Denmark, Deteksi bahasa, Esperanto, Estonia, Farsi, Finlandia, Frisia, Gaelig, Gaelik Skotlandia, Galisia, Georgia, Gujarati, Hausa, Hawaii, Hindi, Hmong, Ibrani, Igbo, Inggris, Islan, Italia, Jawa, Jepang, Jerman, Kannada, Katala, Kazak, Khmer, Kinyarwanda, Kirghiz, Klingon, Korea, Korsika, Kreol Haiti, Kroat, Kurdi, Laos, Latin, Latvia, Lituania, Luksemburg, Magyar, Makedonia, Malagasi, Malayalam, Malta, Maori, Marathi, Melayu, Mongol, Nepal, Norsk, Odia (Oriya), Pashto, Polandia, Portugis, Prancis, Punjabi, Rumania, Rusia, Samoa, Serb, Sesotho, Shona, Sindhi, Sinhala, Slovakia, Slovenia, Somali, Spanyol, Sunda, Swahili, Swensk, Tagalog, Tajik, Tamil, Tatar, Telugu, Thai, Turki, Turkmen, Ukraina, Urdu, Uyghur, Uzbek, Vietnam, Wales, Xhosa, Yiddi, Yoruba, Yunani, Zulu, Bahasa terjemahan.