On the other hand, polymer /montmor

On the other hand, polymer /montmorillonite nanocomposites prepared by solid reaction,
based on grinding MMT with monomers and reagents, have shown an alteration of chemical
structure and properties of the material which are different from that carried out in solution
reaction. For example, in our previous work [7], it was concluded that conducting
polyaniline/MMT nanocomposite prepared by solid reaction presented enhanced electrical
conductivity compared to free polyaniline. In addition it was shown that a ground mixture of
aniline salt and MMT is able to be converted with time to polyaniline clay nanocomposite
without the need to use an external oxidant [8]. On the other hand, the prolonged grinding of
Fe-exchanged MMT with aniline salt favors the formation of a novel crystalline phase of iron
oxide which is normally obtained at high pH [9]. These results demonstrate that grinding
could affect oxidant, acidic and electrical properties of MMT.

Hasil (Bahasa Indonesia) 2:

Di nanocomposites tangan, polimer / montmorillonit lainnya dibuat dengan reaksi yang kuat,
berdasarkan grinding MMT dengan monomer dan reagen, telah menunjukkan perubahan kimia
struktur dan sifat material yang berbeda dari yang dilakukan dalam larutan
reaksi. Misalnya, dalam pekerjaan kami sebelumnya [7], disimpulkan bahwa melakukan
polianilin / MMT nanokomposit dibuat dengan reaksi padat disajikan ditingkatkan listrik
konduktivitas dibandingkan dengan polianilin gratis. Selain itu menunjukkan bahwa campuran dasar
garam anilin dan MMT mampu dikonversi dengan waktu untuk nanokomposit polianilin tanah liat
tanpa perlu menggunakan oksidan eksternal [8]. Di samping itu,
grinding berkepanjangan Fe-ditukar MMT dengan garam anilin mendukung pembentukan fase kristal novel besi
oksida yang biasanya diperoleh pada pH tinggi [9]. Hasil ini menunjukkan bahwa penggilingan
dapat mempengaruhi oksidan, sifat asam dan listrik MMT.